Two-component epoxy-based grout and adhesive.
Two-component, solvent-free epoxy resin-based, high-strength, chemical-resistant,
hygienic grout and ceramic adhesive
General Characteristics
• Excellent resistance to chemicals,
• High resistance to moss and mold formation,
• Suitable for swimming pools.
| Color | Gray & White |
|---|---|
| Appearance | Matte |
| Solids by Weight | % 99 |
| Density | 1,80 gr/cm³ |
| Flash Point | >25°C |
| Mixing Ratio | 3 / 1 |
| Application Methods | Trowel, Spatula |
| Spatula Working Time | 50 minutes / 25°C |
|---|---|
| Layer-to-Layer Waiting Time | 12 hours / 25°C |
| Drying Time | 12 hours / 25°C |
| Flexural Strength | 20 °C de min. 28 N/mm² |
| Adhesion Strength (Concrete Pull-Off) | 3,50 N/mm² (7 days) |
| Compressive Strength | Min. 55 N/mm² at 20°C (7 days) |
It is used on concrete, natural stone, aerated concrete, ceramics, in the restoration of historical buildings, and for filling corner joints, crack expansion holes, and cracks, as well as in areas where chemical resistance is required. It can be easily used on vertical surfaces. Excess material adhering to ceramics or tiles should be cleaned with hot water before it dries.
5 kg (A+B): It should be stored in its unopened original packaging in a cool and dry place, protected from freezing. The appropriate storage temperature should be between +5°C and +25°C. Shelf life: Under proper storage conditions, the shelf life is 12 months from the production date.
During application and mixing, contact with skin and eyes should be avoided. In case of contact, rinse thoroughly with water. If the material comes into contact with the eyes, immediately rinse with plenty of water and seek medical attention. Gloves, protective clothing, masks, and goggles should be worn during use.
Surfaces should be free of grease and dirt. The A and B components should be mixed according to the specified ratio, and the mixture should be stirred for at least 3-4 minutes using a low-speed mixer until a homogeneous mixture is obtained. The mixture is ready for application after preparation.