Cement-Based, Two-Component, Semi-Elastic Waterproofing Material.
Polymer emulsion modified, cement-based, double component, CMO1P class semi-elastic
waterproofing mortar
General Characteristics
• Quick transition to ceramic application,
• Resistance to light pedestrian traffic,
• Flexible waterproofing coating feature.
| Adhesion Strength | (N/mm2) ≥ 1,00 |
|---|---|
| After Thermal Aging | (N/mm2) ≥ 1,00 |
| CO2 Permeability | Sd > 50 m |
| Capillary Water Absorption | (kg.m-2.dk-0,5) ≤ 0,10 |
| Crack Bridging | (mm) ≥ 0,75 |
| Fire Reaction Class | Bs1d0 |
| Consumption | 1,5 – 2,0 kg/m2 |
| TS EN | 14981 |
|---|---|
| Position No | 10.300.2173 |
| Mixing Ratio A/B | 20/5 |
| Number of Coats | 2 – 3 |
| Application Thickness | 2 - 4 mm |
| Waiting Time | 5 – 6 saat |
| Pot Life | ~3 saat |
• Waterproofing of wet areas, • Waterproofing under tiles on terraces, • Waterproofing of water tanks, • Waterproofing of concrete structures buried underground.
Packaging: A: 20 kg Kraft B: 5 kg Bidon The product should be stored in a clean, dry, and moisture-free environment, between +5°C and +35°C, protected from direct sunlight. It should be safeguarded against water, freezing, and extreme weather conditions. It should be stored in a maximum of 10 layers. If the specified storage conditions are followed, the shelf life is a maximum of 12 months from the production date
During application and mixing, direct contact with skin and eyes should be avoided. In case of contact, rinse thoroughly with water. If it comes into contact with the eyes, rinse immediately with plenty of water and seek medical attention. Protec
First, the B liquid component is placed into a container. Then, the entire contents of the A powder component bag are added, and the mixture is stirred continuously for 4-5 minutes. The mixed material is left to rest for 5 minutes, then stirred again until air bubbles disappear, and the application begins. 2C Flex is applied to the concrete surface in at least two layers using a brush. The material placed on the brush is first applied thickly (1st layer), and for achieving the desired thickness and smoothness, the subsequent layers (2nd and 3rd layers) are applied in perpendicular directions. The material should not be spread like paint; it should be applied in one go and horizontally to achieve a good appearance. 2C Flex becomes rain-resistant a few hours after application. It reaches its final strength after 28 days. After application, it should be cured for 24-48 hours. During and after application, the surface should be protected from sunlight, rain, and frost for at least 3 days. Walkable surfaces should be covered with decorative coatings such as screed, tiles, ceramics, or pottery after 3 days.